   If memory serve correct the annealing temp for 6061 is above 900
   degrees. Weld supply shops have temp sticks (like crayon) that melts at
   lable temperatures. hard to get the whole piece to that temp but you
   may be able to do problem spots.

   Did you use 6061 for a specific reason? Mant parts made with the
   english wheel are from 3003 which is dead soft and very easy to form
   compared to 6061 or 5052. It is also weldable by gas flame although I
   still prefere TIG.

   Dan


Two reasons I picked 6061- Everett Hatch recommended it, and it's
available. Also, it's strong. It's worked out pretty well for me so far.
Are there any concerns, other than the fact that it might be a bit
harder to work?

Brian Trubee