Remember these are not final. You will have to do further work on
them. Also double check all dimensions.

Once unzipped they should import into Solid Works.


Paul Lamar


Thanks, Paul.  What shall I tell him for material?

Dave Kingler

6061 T6 is fine.

Paul Lamar

Mild steel okay on the wear plate?  What about the phasing gear?
Dave Kingler

You won't need to make the phasing gear. Stock Mazda part.

The wear plate should be cast iron but that is not practical
starting from scratch. The next best thing is 4130 sheet hardened
surface ground and porous chrome plated. Same as the rotor housing'
liner.

If you band sawed stock Mazda end housings that would work as well.
They too need to be surface ground or milled on the non contact side.

Paul Lamar